<p>[QUOTE=&quot;desertgem, post: 939114, member: 15199&quot;]It could well be so. If it was on the metal before striking, it would tend to be smaller ( thinner) crack on the top of the letter after the strike due to the pressure. If it was produced after the strike ( post strike damage) somehow, it would generally have been wider on the top of the letter. Maybe there is a specific name for it other than lamination, but that is the best I could match <img src="styles/default/xenforo/clear.png" class="mceSmilieSprite mceSmilie1" alt=":)" unselectable="on" unselectable="on" />[/QUOTE]</p><p><br /></p>