I believe this is the best detached lamination I've encountered so far. No idea why the upper edge of the detachment(?) is so straight, though. I'd almost consider it PMD if I didn't see the crack. Thoughts are welcome I tried side lighting this time instead of using the microscope's LEDs. I think the jury's still out on whether this is better or not...
Recently this site has developed a habit of repeating posts. I am officially naming this fault as.................. MACHINE DOUBLING LOL