Sorry, but I can't tell you that.
Perhaps submitting it to Wexler for a highly educated and respected opinion is in your best interest.
If you came here to preach, you found the wrong congregation. Now please go away before you're put away.
Do we have another newbie that will not be happy, and may even be argumentative, unless he gets the answer he seeks?
I disagree with you, Randy, and completely agree with Green.
Are you speaking in tongues?
I know English. I can read it, write it, speak it, and understand it, all very well. That certainly looks like English, but I'll be damned if if I...
Welcome to CT!
The bother was that you insisted that it wasn't PMD before you had any real knowledge of what it was. If you have a question, we will do our best...
It looks like it took a ride around a clothes dryer. PS. Can you use better language? We'd all appreciate it.
I think we need more photos. :D
Someone, many someone's, actually, had to ask their Congresspeople for these in order to get a bill introduced to make them.
What information are you seeking?
Nice pick-up.
It can be overweight (+) or underweight (-) by as much as 0.13 gram and still be within mint specifications.
Oh, I don't know, but I'll take a stab at it. Five cents?
You have very much to learn, Grasshopper.
Can YOU explain how this could happen in the minting process?
1943 pennies were zinc plated steel. The steel was plated before the blanks were punched from the strip, leaving the edge of the coin unplated. If...
It screams reprocessed.