At first I thought it might be a die crack. Under magnification it appears to be a lamination error. It is apparent on the top of the shield. What do you guys think? What do you think this could be worth?
It's just the copper plate peeling away from the zinc core. It will soon be suffering from a terminal case of zinc rot. Spend it before it's gone.