I can see two D's as plain as day. The struck over D is raised enough to reflect light on the curved portion!
There is way to much glare on your photo to tell anything. But there is enough deterioration on the coin to say I seriously doubt it or just plain NO.
Ok... I need the experts on this one. 1943-P War nickel. Is this a lamination problem (or) could this be a transition nickle? I love the striations on both sides.
I don't know what you mean by transition nickel, since the nickels were transitioned in Philly in 1942, but your nickel is simply an improper alloy mix/lamination error. Here's a link for it: http://www.error-ref.com/improper-alloy-mix/ In the future, please start your own thread, or at least wait until the OP's question is answered
Thank you. I thought the question was answered {you need a better picture}. My mistake and I apologize. Thank you for the site it was very helpful.